Centrex ASA 485CS NAT 000000NAT is a Acrylonitrile Styrene Acrylate material and is typically used in Coextrusion, Extrusion, Thermoforming applications. Features include: Good Melt Strength, Good Weather Resistance, Low Gloss, Medium Impact Resistance, and UV Resistant.
ASA 485CS NAT 000000NAT
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (220 °C/10.0 kg) | 5.0 g/10 min |
| Melt Flow Rate (220 °C/10.0 kg) | 6.1 g/10 min |
| Density (23 °C, Method A) | 1.07 g/cm³ |
| Density - Specific Gravity | 1.06 g/cm³ |
| Tensile Modulus (5.1 mm/min) | 1450 MPa |
| Tensile Strength at Yield (5.1 mm/min) | 26.5 MPa |
| Flexural Modulus (1.3 mm/min, Tangent) | 1380 MPa |
| Flexural Strength (1.3 mm/min) | 38.6 MPa |
| Instrumented Dart Impact (23 °C, Total Energy) | 24.0 J |
| Instrumented Dart Impact (-30 °C, Total Energy) | 6.00 J |
| Instrumented Dart Impact (-18 °C, Total Energy) | 16.0 J |
| Notched Izod Impact (-40 °C, 3.18 mm) | 43 J/m |
| Notched Izod Impact (23 °C, 3.18 mm) | 130 J/m |
| Notched Izod Impact (-18 °C, 3.18 mm) | 64 J/m |
| Rockwell Hardness (R-Scale) | 69 |
| Vicat Softening Temperature | 100 °C |
| Deflection Temperature Under Load Unannealed (264 psi) (3.18 mm) | 68.3 °C |
| Coefficent of Linear Thermal Expansion (CLTE), Flow | 9.4E-05 cm/cm/°C |
| Gloss (60°) | 20 |
| Gloss (60°) | 10 |
| Drying Time | 3.0 to 4.0 hr |
| Melt Temperature | 204 to 243 °C |
| Suggested Max Moisture | <0.030 % |
| Die Temperature | 210 to 241 °C |
| Suggested Max Regrind | 40 % |
| Drying Temperature | 82 to 93 °C |
| Flame Rating (1.5 mm) | HB |
| UL File Number (USA) | E150937 |
Technical Data Sheet
Technical Data Sheet - APS ExtrusionProcess
Coextrusion, Extrusion
Resin
Acrylonitrile Styrene Acrylate
Applications
Automotive Applications, Automotive Exterior Parts, Automotive Interior Parts, Exterior Trim, Outdoor Applications