Moplen 2000HEXP

LyondellBasell

Description

Moplen 2000HEXP is a medium fluidity heterophasic copolymer grade for injection moulding applications.
It exhibits an excellent impact performance, particularly at low temperature, combined with a good processability.
Moplen 2000HEXP can be used in luggage, closures and it is an ideal bulding block for technical compounding. It offers a good solution for interior and exterior parts in Automotive compounds.
It is not intended for medical and pharmaceutical applications.
The grade is available in natural, pellet form.

Availability

Africa-Middle East, Europe

Legend

SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin

Product Data and Technical Information

Typical Properties

Melt Flow Rate (230 °C/2.16 kg) 16 g/10 min
Density 0.89 g/cm³
Flexural Modulus 1000 MPa
Tensile Modulus 1000 MPa
Tensile Stress at Break 14 MPa
Tensile Stress at Yield 19 MPa
Tensile Strain at Break 100 %
Tensile Strain at Yield 5 %
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A) 17 kJ/m²
Charpy Impact Strength - Notched (0 °C) 10 kJ/m²
Charpy Impact Strength - Notched (-20 °C, Type 1, Edgewise, Notch A) 8 kJ/m²
Charpy Impact Strength - Notched (-30 °C) 6 kJ/m²
Vicat Softening Temperature (A50) 140 °C
Deflection Temperature Under Load (0.45 MPa, Unannealed) 84 °C
DSC Melting Point 163 °C

Technical Data Sheet

Technical Data Sheet

Process

Compounding, Injection Molding


Resin

Polypropylene, Impact Copolymer


Applications

Automotive Parts, Luggage